Plasmonic Enhancement of Absorption in Sunscreen Applications

ABSTRACT

Zinc oxide compositions as well as techniques for plasmonic enhancement of absorption in sunscreen applications are provided herein. A method includes selecting one or more metal particles to be used in conjunction with one or more zinc oxide particles in a sunscreen composition, wherein said selecting is based on the plasmon resonance frequency associated with each of the metal particles; and embedding the one or more selected metal particles into each of the one or more zinc oxide particles.

FIELD

The present application generally relates to chemical technology, and,more particularly, to sunscreen technologies.

BACKGROUND

Sunscreen creams and other such compositions are commonly used toprevent ultraviolet (UV) radiation (also referred to herein as “light”in this context) from reaching the skin of a human user and causingdamage. It is noted that UV light is an electromagnetic radiation with awavelength range between approximately 280 nanometers (nm) andapproximately 400 nanometers (specifically, that is the range of UVradiation that is not absorbed by the ozone).

A common active ingredient of existing sunscreen compositions is zincoxide (ZnO). ZnO is a semiconductor that has a specific band gap, andparticles of ZnO used in existing sunscreen compositions are typicallyapproximately 50-200 nm in size. Additionally, in existing sunscreencompositions, typical ZnO materials are capable of absorbing UV light(that is, blocking the UV light from passing through the sunscreencomposition to be absorbed by the skin of the user) within a wavelengthrange of approximately 290 nm through only approximately 350-380 nm.

Additionally, high sun protection factor (SPF) sunscreen compositions,which can absorb a large majority of the UV light in the range of290-380 nm, require the addition of a higher density of ZnO particles,which causes the composition to become white and/or opaque due to lightscattering from the ZnO particles, and which is an often undesirableproperty to consumers.

SUMMARY

In one embodiment of the present invention, zinc oxide compositions,methods of fabrications thereof and methods of use thereof are provided.An exemplary method can include selecting one or more metal particles tobe used in conjunction with one or more zinc oxide particles in asunscreen composition, wherein said selecting is based on the plasmonresonance frequency associated with each of the metal particles. Themethod can also include embedding the one or more selected metalparticles into each of the one or more zinc oxide particles.

In another embodiment of the invention, a sunscreen composition caninclude multiple zinc oxide particles suspended within a medium, and oneor more metal particles embedded into each of the multiple zinc oxideparticles, wherein each of the metal particles comprises a plasmonresonance frequency that supplements the light absorption capabilitiesof the multiple zinc oxide particles.

These and other objects, features and advantages of the presentinvention will become apparent from the following detailed descriptionof illustrative embodiments thereof, which is to be read in connectionwith the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagram illustrating a metal particle embedded within a ZnOparticle, according to an example embodiment of the invention;

FIG. 2 is a diagram illustrating ZnO particles, each embedded with ametal particle, embedded within a silicon dioxide (SiO₂) particle,according to an example embodiment of the invention;

FIG. 3 is a diagram illustrating multiple metal particles embeddedwithin a ZnO particle; and

FIG. 4 is a flow diagram illustrating techniques, according to anembodiment of the invention.

DETAILED DESCRIPTION

As described herein, an embodiment of the present invention includes ZnOcompositions as well as techniques for plasmonic enhancement ofabsorption in sunscreen applications. As further detailed herein, one ormore embodiments of the invention include generating ZnO compositionsand methods of use thereof for effectively blocking more and/or all ofthe complete spectrum of UV light (that is, as noted above, the UVradiation that is not absorbed by the ozone, and which ranges betweenapproximately 280 nm and 400 nm) while also preventing whitening effectscaused by the scattering of light in the visible spectrum (that is,radiation between approximately 400 nm and 700 nm). As used herein,“scattering” refers to the deflection of rays of visible light from therays' original path due to interaction with particle surfaces.

At least one embodiment of the invention includes enhancing lightabsorption capabilities of ZnO particles by using plasmonic resonances.As detailed herein and illustrated via the example embodiments depictedin FIGS. 1-3, one or more embodiments of the invention can includegenerating a structure that is designed to utilize the plasmonicenhancement of light intensity near a metal particle surface. In such anembodiment, one or more metal particles are enclosed and/or embeddedinside a ZnO particle to generate plasmonic enhancement of absorption inthe resulting composition.

FIG. 1 is a diagram illustrating a metal particle 104 embedded within aZnO particle 102, according to an example embodiment of the invention.In one or more embodiments of the invention, the metallic and/orplasmonic particle 104 can include a silver (Ag) particle or a gold (Au)particle. Also, in at least one embodiment of the invention, themetallic and/or plasmonic particle 104 can be less than 30 nm indiameter (for example, between 10 and 30 nm in diameter). Additionally,the ZnO particle 102 can be approximately 200 nm in diameter (forexample, between 100 and 200 nm in diameter) to utilize the plasmoniceffect of the metal particle 104 and maximize the plasmonic enhancementabsorption of the resultant composition. In accordance with one or moreembodiments of the invention, the electric field is only enhanced withinapproximately 100 nm of the metallic particle 104.

FIG. 2 is a diagram illustrating ZnO particles 102, each embedded with ametal particle 104, embedded within a SiO₂ particle 202, according to anexample embodiment of the invention. While the example embodimentdepicted in FIG. 2 utilizes a SiO₂ particle 202, it is to be appreciatedthat one or more embodiments of the invention can utilize any materialthat has a large band gap (greater than approximately ˜3.2 electronvolts (eV), for example) and a refractive index in between that of ZnOand air. Additionally, the SiO₂ particle 202, as depicted in the FIG. 2example, can be (approximately) between 0.8-2.0 micrometers in diameter.

FIG. 3 is a diagram illustrating multiple metal particles 104 embeddedwithin a ZnO particle 102. In one or more embodiments of the invention,the distance between metal particles 104 can include any distance amountso as to ensure that the metal particles 104 are physically separatefrom one another. In one example, such as depicted in FIG. 3, thedistance between the metal particles 104 can be approximately 100-200nm. Also, in one or more embodiments of the invention (such as theexample embodiment depicted in FIG. 3), the size of each individual ZnOparticle 102 can be reduced (for use in a sunscreen composition) to lessthan 400 nm. By way of example, at least one embodiment of the inventionincludes reducing the size of each ZnO particle to a size of betweenapproximately 100 and 400 nm.

Further, it is noted that the example ZnO particle depicted in FIG. 3(embedded with multiple metal particles) can also be utilized asillustrated in FIG. 2; that is, the example ZnO particle depicted inFIG. 3 (embedded with multiple metal particles) can be embedded within aSiO₂ particle 202, in accordance with one or more embodiments of theinvention.

FIG. 4 is a flow diagram illustrating techniques, according to anembodiment of the present invention. Step 402 includes selecting one ormore metal particles to be used in conjunction with one or more zincoxide particles in a sunscreen composition, wherein said selecting isbased on the plasmon resonance frequency associated with each of themetal particles. Step 404 includes embedding the one or more selectedmetal particles into each of the one or more zinc oxide particles.

In at least one embodiment of the invention, each of the zinc oxideparticles can include a size of less than 400 nanometers in diameter,and each of the one or more metal particles can include a size of lessthan 30 nanometers. Additionally, the one or more metal particles caninclude one or more silver particles and/or one or more gold particles.Further, in one or more embodiments of the invention, the one or moremetal particles can include multiple metal particles, wherein themultiple metal particles are each physically separated within each ofthe one or more zinc oxide particles.

The techniques depicted in FIG. 4 can also include selecting one or moresuspension particles to be utilized in conjunction with the multiplezinc oxide particles, wherein each of the one or more suspensionparticles is larger in size than each of the multiple zinc oxideparticles, and wherein said selecting is based on the refractive indexof each of the one or more suspension particles. One or more embodimentsof the invention can also include embedding the multiple zinc oxideparticles into the one or more suspension particles. Additionally, insuch an embodiment, the one or more suspension particles can include oneor more silicon dioxide particles, and each of the one or moresuspension particles can include a size of between 0.8 and 2micrometers. Further, in at least one embodiment of the invention, therefractive index of each of the one or more suspension particles isbetween that of air and zinc oxide.

Also, an additional embodiment of the invention includes a sunscreencomposition that includes multiple zinc oxide particles suspended withina medium, and one or more metal particles embedded into each of themultiple zinc oxide particles, wherein each of the metal particlescomprises a plasmon resonance frequency that supplements the lightabsorption capabilities of the multiple zinc oxide particles. Such acomposition can also include one or more suspension particles, whereineach of the one or more suspension particles is larger in size than eachof the multiple zinc oxide particles, and wherein each of the multiplezinc oxide particles is embedded into the one or more suspensionparticles.

The terminology used herein is for the purpose of describing particularembodiments only and is not intended to be limiting of the invention. Asused herein, the singular forms “a,” “an” and “the” are intended toinclude the plural forms as well, unless the context clearly indicatesotherwise. It will be further understood that the terms “comprises”and/or “comprising,” when used in this specification, specify thepresence of stated features, steps, operations, elements, and/orcomponents, but do not preclude the presence or addition of anotherfeature, step, operation, element, component, and/or group thereof.

At least one embodiment of the present invention may provide abeneficial effect such as, for example, generating a structure that isdesigned to utilize the plasmonic enhancement of light intensity near ametal particle surface.

The descriptions of the various embodiments of the present inventionhave been presented for purposes of illustration, but are not intendedto be exhaustive or limited to the embodiments disclosed. Manymodifications and variations will be apparent to those of ordinary skillin the art without departing from the scope and spirit of the describedembodiments. The terminology used herein was chosen to best explain theprinciples of the embodiments, the practical application or technicalimprovement over technologies found in the marketplace, or to enableothers of ordinary skill in the art to understand the embodimentsdisclosed herein.

What is claimed is:
 1. A method, comprising: selecting one or more metalparticles to be used in conjunction with one or more zinc oxideparticles in a sunscreen composition, wherein said selecting is based onthe plasmon resonance frequency associated with each of the metalparticles; and embedding the one or more selected metal particles intoeach of the one or more zinc oxide particles.
 2. The method of claim 1,further comprising: selecting one or more suspension particles to beutilized in conjunction with the multiple zinc oxide particles, whereineach of the one or more suspension particles is larger in size than eachof the multiple zinc oxide particles, and wherein said selecting isbased on the refractive index of each of the one or more suspensionparticles.
 3. The method of claim 2, further comprising: embedding themultiple zinc oxide particles into the one or more suspension particles.4. The method of claim 2, wherein the one or more suspension particlescomprise one or more silicon dioxide particles.
 5. The method of claim2, wherein each of the one or more suspension particles comprises a sizeof between 0.8 and 2 micrometers.
 6. The method of claim 2, wherein therefractive index of each of the one or more suspension particles isbetween that of air and zinc oxide.
 7. The method of claim 1, whereineach of the zinc oxide particles comprises a size of less than 400nanometers in diameter.
 8. The method of claim 1, wherein the one ormore metal particles comprise one or more silver particles and/or one ormore gold particles.
 9. The method of claim 1, wherein each of the oneor more metal particles comprises a size of less than 30 nanometers. 10.The method of claim 1, wherein the one or more metal particles comprisemultiple metal particles, and wherein the multiple metal particles areeach physically separated within each of the one or more zinc oxideparticles.
 11. A sunscreen composition comprising: multiple zinc oxideparticles suspended within a medium; and one or more metal particlesembedded into each of the multiple zinc oxide particles, wherein each ofthe metal particles comprises a plasmon resonance frequency thatsupplements the light absorption capabilities of the multiple zinc oxideparticles.
 12. The composition of claim 11, further comprising: one ormore suspension particles, wherein each of the one or more suspensionparticles is larger in size than each of the multiple zinc oxideparticles, and wherein each of the multiple zinc oxide particles isembedded into the one or more suspension particles.
 13. The compositionof claim 12, wherein each of the one or more suspension particles isselected based on the refractive index of each of the one or moresuspension particles.
 14. The composition of claim 12, wherein the oneor more suspension particles comprise one or more silicon dioxideparticles.
 15. The composition of claim 12, wherein each of the one ormore suspension particles comprises a size of between 0.8 and 2micrometers.
 16. The composition of claim 12, wherein the refractiveindex of each of the one or more suspension particles is between that ofair and zinc oxide.
 17. The composition of claim 11, wherein each of thezinc oxide particles comprises a size of less than 400 nanometers indiameter.
 18. The composition of claim 11, wherein the one or more metalparticles comprise one or more silver particles and/or one or more goldparticles.
 19. The composition of claim 11, wherein each of the one ormore metal particles comprises a size of less than 30 nanometers. 20.The composition of claim 11, wherein the one or more metal particlescomprise multiple metal particles, and wherein the multiple metalparticles are each physically separated within each of the one or morezinc oxide particles.